BONDING OF LAMINATE VENEER MATERIALS TO ENAMEL
BONDING OF LAMINATE VENEER MATERIALS TO ENAMEL
 
لغة الوثيقة : الانجليزية 
المستخلص : The purpose of this study is to examine the effect of enamel surface pretreatment on the shear bond strength of tooth colored restorative materials bonded to human enamel with different luting systems. Forty-two extracted human molars were used in this study. Buttons, 6 x 3 mm., of two types of composite resin (Silux# & Visio-Gem@) and 5 x 3 mm. buttons of dental porcelain, were prepared. The prepared buttons were attached to the buccal, lingual and proximal surfaces of extracted molars. The enamel surfaces were cut in some groups while left uncut in other groups. One, or a combination of two, of the following luting materials was used with the composite resin groups: Chemically-cured Scotchbond# ; Lightcured Scotchbond# ; Visio-Gem ; Visio-Gem Glaze@ and Conc1ude@. For the porcelain groups, Scotchprime#, Conclude, Silux, and Visio-Gem were used as luting materials. Samples were tested on an Instron testing machine. Single factor analysis of variance of the data obtaincd that: a) In the silux groups there is no significant difference in shear bond strength between cut and uncut enamel with diffe(ent luting systems; b) Among the Visio-Gem groups the highest shear bond strength is obtained with the cut enamel surface when a combination of Visio-Gem and Visio-Gem Glazc was used asluting material; c) TIle porcelain groups show the highest shear bond strength with the enamel surfaces trimmed flat and the usc of a combination of Scotchprimc and Conclude as luting material. * 
ردمد : 0 
اسم الدورية : المجلة المصية لطب الاسنان 
المجلد : 40 
العدد : 1 
سنة النشر : 1994 هـ
1994 م
 
نوع المقالة : مقالة علمية 
تاريخ الاضافة على الموقع : Sunday, February 7, 2010 

الباحثون

اسم الباحث (عربي)اسم الباحث (انجليزي)نوع الباحثالمرتبة العلميةالبريد الالكتروني
فاضل عثمانOthman, Fadil باحث مشاركدكتوراه 

الملفات

اسم الملفالنوعالوصف
 25230.pdf pdf 

الرجوع إلى صفحة الأبحاث